https://www.selleckchem.com/products/itf3756.html
645). Both A and AL increased monoclinic phase content for 3Y and 4Y FDPs, whereas FIB-SEM suggests no transformability of 5Y-PSZ. 5Y-AL FDPs showed cracks and fractures at the abutment walls and restoration margins after dynamic loading. Reduced fracture load of 5Y samples as compared to 3Y and 4Y was associated with deficient transformability in the fracture zone. Aging and loading did not negatively affect the fracture resistance of monolithic four-unit FDPs made from three grades of zirconia. Due to cracks after dynamic loading, 5Y-