The low yield strength (~300 MPa) of twinning-induced plasticity (TWIP) steels greatly limits their structural applications in the industrial field. Conventional strengthening mechanisms usually cause an enhancement of yield strength but also a severe loss of ductility. In this research, gradient substructures were introduced in the Fe-22Mn-0.6C TWIP steels by different pre-torsional deformation in order to overcome the above limitations. The substructure evolution, mechanical properties, and their origins in gradient-substruc