To investigate the impact of pretreatment and conditioning on shear bond strength (SBS), surface free energy (SFE) and surface roughness (SR) between polyetheretherketone (PEEK) and cold-cured polymethylmethacrylate (PMMA). PEEK substrates (Dentokeep PEEK Disc, nt-trading) were air abraded with Al2O3 particles of different grain sizes applied with varying pressure at 1) 0.2 MPa - 50 µm Al2O3; 2) 0.4 MPa - 50 µm Al2O3; 3) 0.2 MPa - 110 µm Al2O3; 4) 0.4 MPa - 110 µm Al2O3; or 5) without air abrasion (n = 172/group). Surface propertie