In this paper, the Ni-Nb coatings were successfully prepared onto the GH3039 alloys by High current pulsed electron beam (HCPE. The transmission electron microscopy (TEM) results confirmed that the Ni-Nb layer of 10-pulsed samples exhibited partial amorphization, which was consisted of γ-Ni particles, rod-like Ni3Nb particles and nano Ni3Nb with 30 nm in size. After 20-pulsed irradiation, the results show that only Ni3Nb clusters with around 3 nm in size were dispersed in fully amorphization layer. With increased pulse number to 30, t