Mg-15Gd-1Zn (wt.%) alloy was successfully prepared via the spark plasma sintering rapid solidification ribbons process. Microstructure investigation showed that the sintered alloys consisted of fine grains, the β1 phase, and long-perioded stacking ordered phase (LPSO). The sintering temperature and time have a significant effect on the microstructural evolution. A lower sintering temperature (430 °C ) was beneficial for obtaining finer grain sizes with less than 5 μm and a higher content of β1 phase with a content of 3-15 vol.% and a size-distribution of (1