Ti(C,N)-reinforced alumina-zirconia composites with different ratios of C to N in titanium carbonitride solid solutions, such as Ti(C0.3,N0.7) (CN = 307 and Ti(C0.5,N0.5) (CN = 505, were tested to improve their mechanical properties. Spark plasma sintering (SPS) with temperatures ranging from 1600 °C to 1675 °C and pressureless sintering (PS) with a higher temperature of 1720 °C were used to compare results. The following mechanical and physical properties were determined Vickers hardness, Young's modulus, apparent density, wear res