The obtained results show that the local stresses in Al matrix having no precipitates were in the range of 138 ± 2 MPa. Whereas, in the vicinity of thin and thick T1 platelet shape precipitates, the stresses were found to be about 202 ± 3 MPa and 195 ±3 MPa, respectively. The stresses measured in the vicinity of β' spherical shape precipitates found out to be 140 ± 3 MPa which was near to the local stress value in Al matrix. Our findings suggest that the precipitate hardening in T8 temper AA2195 Al alloy predominantly stems from thin T