After I2(g) capture, the AgI crystallites were observed in the sorbent, verifying chemisorption as the primary iodine capture mechanism. Iodine loading of this xerogel was 0.43 g g-1 at 150 °C over 1 day and 0.52 g g-1 at 22 °C over 33 days. The specific surface area of Ag-HTX was 202 m2 g-1 and decreased to 87 m2 g-1 after iodine loading. The hardness of the Na-HTX was 145 times higher than that of the heat-treated aerogel of the same starting composition. The heat-treatment process increased Young's modulus (compressive) value to 4