In the present study, the phase constitution, microstructure and magnetic properties of the nanocrystalline magnets, derived from fully amorphous or partially crystalline samples by annealing, were analyzed and compared. The melt-spun ribbons (with a thickness of ~30 µm) and suction-cast 0.5 mm and 1 mm thick plates of the Pr9Fe50Co13Zr1Nb4B23 alloy were soft magnetic in the as-cast state. In order to modify their magnetic properties, the annealing process was carried out at various temperatures from 923K to 1033K for 5 min.