Silicon anodes are considered as promising electrode materials for next-generation high capacity lithium-ion batteries (LIBs). However, the capacity fading due to the large volume changes (∼300%) of silicon particles during the charge-discharge cycles is still a bottleneck. The volume changes of silicon lead to a fracture of the silicon particles, resulting in recurrent formation of a solid electrolyte interface (SEI) layer, leading to poor capacity retention and short cycle life. Nanometer-scaled silicon particles are the favorable anod