Thermoelastic deformation mechanisms in polycrystalline biomedical-grade superelastic NiTi are spatially mapped using in situ neutron diffraction during multiaxial loading and heating. The trigonal R-phase is formed from the cubic phase during cooling to room temperature and subsequently deforms in compression, tension, and torsion. The resulting R-phase variant microstructure from the variant reorientation and detwinning processes are equivalent for the corresponding strain in tension and compression, and the variant microst