The aim of this study is to evaluate the color alteration and shore A hardness of a medical silicone with extrinsic pigmentation, before and after accelerated aging. Twenty samples (Silastic Q7-4735) were made with an intrinsic pigmentation. This intrinsic pigmentation was composed of a pink pigment (H-109-P, Factor II) and an opacifier (ZnO). All samples had standardized dimensions (45-mm diameter and 2-mm thickness). Half of the 20 samples manufactured subsequently received an extrinsic pigment (Tan FE-215, Factor II). Therefore,